Grinding Roller Tyre for Pulverizer Mill
Material: High Chrome White Iron
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
Grinding Table Segment
Material: High Chrome White Iron
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Weight: ~750 kg each segment
Note: Chemical composition can be varied based on customer's request
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Weight: ~750 kg each segment
Note: Chemical composition can be varied based on customer's request
Grinding Roller Segment for Cement Mill
Material: High Chrome White Iron
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 59 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
Tower Mill Liner
Material: 25%Cr (ASTM A 532/A 532M -93a)
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
High Chrome White Iron Mantle
Material: 20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Size: ID1100 mm, OD1400 mm, Height 500 mm
Note: Chemical composition can be varied based on customer's request
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Size: ID1100 mm, OD1400 mm, Height 500 mm
Note: Chemical composition can be varied based on customer's request
High Chrome White Iron Air Ports: (Upper)
Material: Ni-Hard 1
Casting method: Sand cast
Hardness: 53-61 HRC after quenching
Note: Chemical composition can be varied based on customer's request
Casting method: Sand cast
Hardness: 53-61 HRC after quenching
Note: Chemical composition can be varied based on customer's request
High Chrome White Iron Grinding Disk
Material: 25%Cr (ASTM A 532/A 532M -93a)
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
High Chrome White Cast Iron Damp Covers
Material: 20%Cr-Mo (ASTM A 532/A 532M-93a)
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
G-X260CrMoNi20 2 1(DIN1695-81)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request
High Chromium Cast Iron Body Liner
Material: 25%Cr (ASTM A 532/A 532M -93a)
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request.
G-X300CrMo27 1(DIN1695)
Casting method: Sand cast
Hardness: As cast: ~46 HRC
Hardened, min: 58 HRC
Softened, max: 41 HRC
Note: Chemical composition can be varied based on customer's request.
Prev
1
2
Next
Messages
Please leave your valuable comments or suggestions and contact information (email or telephone), so that we can reply to you in time!
客户留言
Description:
QR code
Scan QR code
Copyright © Shenyang Gongda Heavy Equipment Manufacturing Co., Ltd., All Rights Reserved. 辽ICP备05007835号 Powered by 300.cn SEO标签导航